Bergolin 2C Aqua Clear Coat 2D4200
Description
Bergolin 2C Aqua Clear Coat 2D4200, colorless, is a matte, water-dilutable, low-VOC two-component polyurethane clear coat with anti-slip properties for coating high-quality visible carbon fiber components made of CFRP and GFRP. The coating cures to a non-slip, matte surface with a unique texture that ensures a firm, secure grip, while drying quickly, allowing for immediate recoating, and showcasing the fiber structure. As a water-dilutable, low-solvent system, the product enables low-emission application; it is applied with a cup gun to mechanically sanded CFRP and GFRP substrates. Typical applications include non-slip, matte visible carbon fiber surfaces on sports and recreational equipment, as well as anywhere where a slip-resistant, secure-grip, and matte surface is required.
Recommended use
- A matte, non-slip clear coat finish on high-quality exposed carbon fiber components made of CFRP and GFRP
- Non-slip, grippy surfaces on sports and recreational equipment
- A visible, distinct fiber structure combined with a matte finish—ideal for exposed carbon fiber designs
- Low-emission clear coat application in composite manufacturing and paint shops (application using a cup gun)
- All applications that require a slip-resistant and matte surface
Product details
- Chemical composition: Polyurethane, water-dilutable (two-component system)
- Hardener system: Bergolin Hardener 7D4200
- Characteristics: water-dilutable, non-slip, quick-drying, can be painted over immediately, low VOC
- Color: colorless
- Finish: matte
- Mixing ratio: 15–20% water
- Cleaning diluent: Water, followed by Superdur Thinner 5D402
- Mixing ratio: 100 : 10 by weight
- Density: approx. 1.09 g/cm³ (mixture, DIN EN ISO 2811-1, +20 °C)
- Solid content: approx. 66% by weight (mixture)
- VOC content: Low VOC (see safety data sheet for details)
- Pot life: approx. 8 hours at +20 °C and 50% relative humidity
- Curing time: > 6 hours at +20 °C and 50% relative humidity
- Drying: dust-dry (TG 1) after approx. 1 hour; can be recoated with the same product immediately up to a maximum of 72 hours
- Application temperature: +5 °C to +25 °C (accelerated curing above +20 °C)
- Shelf life: approx. 12 months in the original, unopened container at temperatures between +4 °C and +40 °C; protect from frost and moisture
- Compatible Systems: CFRP/GFRP substrates (other substrates available upon request)
Advantages at a glance
- Water-dilutable and low in VOCs – low-emission, solvent-reduced application
- The anti-slip feature ensures a firm, secure grip
- Matte finish with a unique texture and a high-quality visible carbon fiber look
- Quick-drying—dust-dry after about 1 hour, short cycle times in production
- Can be reworked immediately for up to 72 hours—flexible process planning without intermediate sanding
- A long pot life of about 8 hours allows for relaxed work on larger batches
- Easy application using a cup gun with low material consumption (approx. 70 g/m² for 50 µm)
Similar products
Bergolin Putty 4D9700-HighTemp
Bergolin Putty 4D9700-HighTemp is a solvent-free, elastic two-component polyurethane filler for wind turbine rotor blades, offering a sufficiently long working time up to +45 °C—short sanding times, lightfast, and easy to apply using a two-component cartridge.
Bergolin Putty 4D9700-LowTemp
Bergolin Putty 4D9700-LowTemp is a solvent-free, flexible two-component polyurethane filler for wind turbine rotor blades that cures reliably at temperatures as low as +5 °C—it allows for short sanding times even in cold conditions, is lightfast, and can be applied using a two-component cartridge.
Steodur PUR Gelcoat 6D970-3
Steodur PUR Gelcoat 6D970-3 is a solvent-free, lightfast two-component polyurethane gelcoat for wind turbine rotor blades, featuring integrated UV absorbers for temporary outdoor storage—it sands very well, provides a pore-free base for subsequent coatings, and is OEM-approved.