Bergolin 2K Aqua Shop Primer 3E6100
Description
Bergolin 2K Aqua Shopprimer 3E6100 is a water-based, two-component epoxy shop primer for priming pre-cleaned or sandblasted steel substrates. The system was developed for cost-effective use in industrial steel manufacturing and provides excellent corrosion protection even at low film thicknesses. The coating is characterized by very good adhesion and fast drying, and is suitable for welding. It can be applied cost-effectively using Airmix application and, thanks to its water-based formulation, has a low VOC content.
Recommended use
- Shop primer or primer coat for pre-cleaned or sandblasted steel substrates
- Corrosion Protection in Industrial Steel Manufacturing
- Weldable primer for further processing
- Cost-effective Airmix series coating with low VOC content
Product details
- Chemical composition: Epoxy resin system (two-component, water-based)
- Hardener system: Bergolin Hardener 7E6000
- Characteristics: water-based, good corrosion protection, excellent adhesion, quick-drying, suitable for welding
- Color: gray, green (other colors available upon request)
- Density: Mixture approx. 1.31 g/mL
- VOC content: approx. 42.1 g/l (mixture)
- Solids: approx. 54.5% by weight (mixture)
- Coverage: approx. 65 g/m² (mixture) at a dry film thickness of 20 µm
- Coating thickness: approx. 25 µm TSD / 50 µm NSD
- Working time: approx. 2 hours
- Drying: touch-dry in approx. 4 min; fully dry in approx. 220 min (50 µm NSD); forced drying possible
- Application temperature: +15 °C to +35 °C
- Shelf life: 12 months in the original, unopened container at temperatures between +4 °C and +40 °C; protect from frost and moisture
- Approvals / Standards: Welding qualification test in accordance with DIN EN ISO 17652-2:2003-07 (DVS SLV Duisburg, Test Report 2402.P0309A); DNV-GL Type Approval (Certificate TAK00002E0)
Advantages at a glance
- Excellent corrosion protection even at low coating thicknesses
- Very fast drying (dust-dry in about 4 minutes) for high throughput rates
- Suitable for welding – tested in accordance with DIN EN ISO 17652-2
- DNV-GL Type Approval for Use in Shipbuilding and Plant Engineering
- Aqueous formulation with low VOC content (approx. 42.1 g/l)
- Excellent adhesion to shot-blasted steel
- Cost-Effective Airmix Application
Similar products
Bergolin Putty 4D9700-HighTemp
Bergolin Putty 4D9700-HighTemp is a solvent-free, elastic two-component polyurethane filler for wind turbine rotor blades, offering a sufficiently long working time up to +45 °C—short sanding times, lightfast, and easy to apply using a two-component cartridge.
Bergolin Putty 4D9700-LowTemp
Bergolin Putty 4D9700-LowTemp is a solvent-free, flexible two-component polyurethane filler for wind turbine rotor blades that cures reliably at temperatures as low as +5 °C—it allows for short sanding times even in cold conditions, is lightfast, and can be applied using a two-component cartridge.
Steodur PUR Gelcoat 6D970-3
Steodur PUR Gelcoat 6D970-3 is a solvent-free, lightfast two-component polyurethane gelcoat for wind turbine rotor blades, featuring integrated UV absorbers for temporary outdoor storage—it sands very well, provides a pore-free base for subsequent coatings, and is OEM-approved.