Pekinol Primer 3A310-F
Description
Pekinol Primer 3A310-F, RAL 9002 is a solvent-based, fast-drying, single-component primer based on a modified alkyd resin that provides good corrosion protection for steel substrates. It has a thixotropic consistency, allowing it to be applied in thick coats without sagging. Its fast drying time enables short cycle times and rapid recoating within the coating system. The primer forms a durable base for subsequent topcoats.
Recommended use
- Anti-corrosion primer for steel structures
- Thick-film primer with a dry film thickness of up to approximately 80 µm in a single pass
- Priming of vertical surfaces thanks to thixotropic properties
- Application with a brush, roller, or airless/airmix sprayer
- A stable base for subsequent Bergolin topcoats
Product details
- Chemical composition: modified alkyd resin (1-component system)
- Characteristics: Corrosion protection, single-component, high-build, fast-drying, thixotropic
- Color: RAL 9002 (other colors available upon request)
- Finish: matte
- VOC content: approx. 415 g/l
- Max. coating thickness: approx. 80 µm dry film thickness at approx. 220 g/m²
- Drying: dust-dry in approx. 45 min; fully dry in approx. 70 min; can withstand full loads after complete curing, approx. 7 days
- Shelf life: approx. 12 months in the original, unopened container (+4 °C to +40 °C); protect from heat and cold
- Compatible Systems: Can be combined with numerous other Bergolin products to form a coordinated coating system—select a system through Technical Service
Advantages at a glance
- Good corrosion protection on steel substrates
- Thixotropic consistency—can be applied in a thick layer without running
- Quick-drying – touch-dry in about 45 minutes, fully dry in about 70 minutes
- Short turnaround times and quick revisions (starting at 12 hours)
- High solid content of approximately 70% by weight – high material yield
- Can be applied flexibly with a brush, roller, or airless/Airmix sprayer
- Can be applied at temperatures as low as +5 °C
Similar products
Bergolin Putty 4D9700-HighTemp
Bergolin Putty 4D9700-HighTemp is a solvent-free, elastic two-component polyurethane filler for wind turbine rotor blades, offering a sufficiently long working time up to +45 °C—short sanding times, lightfast, and easy to apply using a two-component cartridge.
Bergolin Putty 4D9700-LowTemp
Bergolin Putty 4D9700-LowTemp is a solvent-free, flexible two-component polyurethane filler for wind turbine rotor blades that cures reliably at temperatures as low as +5 °C—it allows for short sanding times even in cold conditions, is lightfast, and can be applied using a two-component cartridge.
Steodur PUR Gelcoat 6D970-3
Steodur PUR Gelcoat 6D970-3 is a solvent-free, lightfast two-component polyurethane gelcoat for wind turbine rotor blades, featuring integrated UV absorbers for temporary outdoor storage—it sands very well, provides a pore-free base for subsequent coatings, and is OEM-approved.