Steodur PUR Machine-Application Filler (Thix) 6D978
Description
Steodur PUR Machine Filler (Thix) 6D978 is a solvent-free, elastic, and lightfast two-component polyurethane filler for wind turbine rotor blades. As a thixotropic, ultra-lightweight filler with a mixed density of approximately 0.87 g/cm³, it levels out surface irregularities and creates a smooth, flexible, and lightfast base for further coating. It is applied using a two-component dispensing system; since no air is incorporated during the application process, no open pores remain after sanding.
Recommended use
- Machine-Applied Coating of Wind Turbine Rotor Blades
- Weight-optimized leveling of surface irregularities on fiberglass-reinforced plastic (FRP) components (other substrates available upon request)
- Creating a smooth, elastic, and lightfast base for subsequent coatings
- Mass production using 2K dispensing systems with short cycle times
Product details
- Chemical composition: Polyurethane (two-component system)
- Hardener system: Steodur PUR Hardener 7D080-SW (black)
- Characteristics: solvent-free, elastic, lightfast, thixotropic, quick-drying
- Color: approx. RAL 6021 (other colors available upon request)
- Finish: glossy
- VOC content: approx. 6 g/l (mixture, IE Directive 2010/75/EU); Component A approx. 9 g/l, Component B approx. 0 g/l
- Density: approx. 0.87 g/cm³ (mixture, DIN EN ISO 2811-1, +20 °C)
- Solids: approx. 99% by weight
- Working time: approx. 2.5 min
- Processing time: approx. 3 min
- Drying: Can be sanded after about 30 minutes
- Mixing ratio: Comp. A : B = 100 : 60 by weight │ 2.5 : 1 by volume
- Theoretical coverage: approx. 0.87 kg/m² per 1,000 µm dry film thickness
- Application method: Spatula (2-component dispensing system)
- Substrate: FRP (other substrates available upon request)
- Verarbeitungsbedingungen: Lufttemperatur +8 °C bis +30 °C; Luftfeuchte < 85 % rel.; Taupunkt mind. 3 °C unter Objekttemperatur
- Cleaning Dilution: Thinner 5P1100
- Shelf life: approx. 12 months in the original, unopened container at temperatures between +4 °C and +40 °C; protect from frost and moisture
Advantages at a glance
- Ultra-lightweight formulation with approximately 0.87 g/cm³—low material application and low sheet weight
- Solvent-free – low-emission application with approximately 6 g/l VOC
- Elastic and lightfast—a permanently stable base for rotor blade coatings
- Thixotropic – stays in place even on vertical surfaces
- No open pores after sanding thanks to air-free system processing
- Quick-drying—can be sanded after about 30 minutes, resulting in short cycle times
- Mixing errors are made visible and can be prevented by the black hardener
Similar products
Bergolin Putty 4D9700-HighTemp
Bergolin Putty 4D9700-HighTemp is a solvent-free, elastic two-component polyurethane filler for wind turbine rotor blades, offering a sufficiently long working time up to +45 °C—short sanding times, lightfast, and easy to apply using a two-component cartridge.
Bergolin Putty 4D9700-LowTemp
Bergolin Putty 4D9700-LowTemp is a solvent-free, flexible two-component polyurethane filler for wind turbine rotor blades that cures reliably at temperatures as low as +5 °C—it allows for short sanding times even in cold conditions, is lightfast, and can be applied using a two-component cartridge.
Steodur PUR Gelcoat 6D970-3
Steodur PUR Gelcoat 6D970-3 is a solvent-free, lightfast two-component polyurethane gelcoat for wind turbine rotor blades, featuring integrated UV absorbers for temporary outdoor storage—it sands very well, provides a pore-free base for subsequent coatings, and is OEM-approved.